Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1494X02 TORAY JAPAN
Toraycon®
Automotive sector,Electronic field,Electrical field
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 82 M（Scale） |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| Water absorption rate | 23℃·24小时 | ASTM D-570 | 0.08 % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 缺口，-40℃ | ASTM D-256 | 3.0 kg·cm/cm |
| ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in | ||
| bending strength | ASTM D790/ISO 178 | 95 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D-256 | 3.5 kg·cm/cm |
| Flexural modulus | ASTM D790/ISO 178 | 2800 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.5 kJ/m² |
| compressive strength | 23℃ | ASTM D-695 | 930 kg/cm |
| Tensile modulus | 23°C | ISO 527-2 | 3000 Mpa |
| elongation at break | ASTM D638/ISO 527 | 20 % | |
| Rockwell hardness | ASTM D785 | M86 | |
| tensile strength | ASTM D638/ISO 527 | 65 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 无缺口，23℃ | ASTM D-256 | 120 kg·cm/cm |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 66 kJ/m² |
| bending strength | 23°C | ISO 178 | 105 Mpa |
| elongation at break | 23℃ | ASTM D-638 | 20 % |
| bending strength | 23℃ | ASTM D-790 | 940 kg/cm |
| Flexural modulus | 23°C | ISO 178 | 2900 Mpa |
| 23℃ | ASTM D-790 | 28 kg/cm | |
| tensile strength | 23℃ | ASTM D-638 | 620 kg/cm |
| Rockwell hardness | ASTM D-785 | 119 | |
| elongation at break | 23°C | ISO 527-2 | 8.0 % |
| Impact strength of cantilever beam gap | 无缺口，-40℃ | ASTM D-256 | 50 kg·cm/cm |
| tensile strength | 23°C | ISO 527-2 | 64.0 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 26 KV/mm | |
| 短时·23℃·1/8时 | ASTM D-149 | 17 KV/mm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.4 | |
| 23°C | IEC 60250 | 3.40 1MHz | |
| Dissipation Factor | 23°C | IEC 60250 | 0.020 1MHz |
| Volume resistivity | ASTM D-257 | 1.0 cm×10 | |
| ASTM D257/IEC 60093 | 1.0x10^14 Ω.cm | ||
| arc resistance | ASTM D-495 | 70 秒 | |
| Volume resistivity | IEC 60093 | 2E+16 Ω.cm | |
| Dissipation Factor | 耐电弧性 | IEC 61621 | 70.0 S |
| other | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| characteristic | 非增强阻燃等级.V-0 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.43 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 1.50mm | |
| UL -94 | V-0 0.71mm | ||
| UL -94 | V-0 3.00mm | ||
| UL -94 | V-0 0.38mm |
| physical property | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| Heat distortion temperature | 18.6kg/cm | ASTM D-648 | 60 °C |
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.080 % |
| coefficient of friction | 本身 | ASTM D-1894 | 0.18 |
| Shrinkage rate | TD | ISO 294-4 | 2.0 % |
| MD | ISO 294-4 | 1.5 % | |
| coefficient of friction | 金属 | ASTM D-1894 | 0.14 |
| Taber abraser | 1.000g·CS-17轮 | ASTM D-1044 | 13 毫克/1.000m |
| Heat distortion temperature | 4.6kg/cm | ASTM D-648 | 165 °C |
| Shrinkage rate | 80×80×3板材 | 1.5-2.0 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1494X02 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 64.0 °C |
| Linear coefficient of thermal expansion | ASTM D-696 | 9.0 cm/cm℃×10 | |
| MD | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 136 °C |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 9.0x10^-5 mm/mm.℃ |