Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS TS201 HF02 TOYOBO JAPAN
--
--
dimensional stability 、High rigidity、Filler: Glass mineral
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TOYOBO JAPAN/TS201 HF02 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | TOYOBO JAPAN/TS201 HF02 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 21600 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.4 % |
| bending strength | 屈服 | ASTM D790 | 234 Mpa |
| tensile strength | 屈服 | ASTM D638 | 170 Mpa |
| Flexural modulus | ASTM D790 | 18600 Mpa |
| Electrical performance | Test Condition | Test Method | TOYOBO JAPAN/TS201 HF02 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1kHz | ASTM D150 | 0.055 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric constant | 1kHz | ASTM D150 | 5.10 |
| Dissipation Factor | 1MHz | ASTM D150 | 8.5E-03 |
| dielectric strength | ASTM D149 | 11 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 4.50 |
| arc resistance | ASTM D495 | 137 sec |
| flammability | Test Condition | Test Method | TOYOBO JAPAN/TS201 HF02 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TOYOBO JAPAN/TS201 HF02 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.15 % |
| Water absorption rate | 24hr | ASTM D570 | 0.020 % |
| Shrinkage rate | TD | ASTM D955 | 0.45 % |
| Thermal performance | Test Condition | Test Method | TOYOBO JAPAN/TS201 HF02 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 260 °C |
| Linear coefficient of thermal expansion | TD | ASTM D696 | 4.8E-05 cm/cm/°C |
| MD | ASTM D696 | 1.2E-05 cm/cm/°C |