POM F10-05 MITSUBISHI THAILAND
Iupital™ 
Electronic and Electrical、Automotive sector
Weather resistance、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/F10-05
Impact strength of simply supported beam without notch23°CISO 179280 kJ/m²
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/F10-05
dielectric strength1.00mmIEC 60243-132 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
relative permittivity100HzIEC 602503.90
Dissipation Factor100HzIEC 602502E-03
dielectric strength3.00mmIEC 60243-119 KV/mm
relative permittivity1MHzIEC 602503.90
Surface ResistivityIEC 600931E+16 ohms
Dissipation Factor1MHzIEC 602507E-03
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/F10-05
Tensile modulusISO 527-22800 Mpa
Nominal tensile fracture strainISO 527-233 %
bending strengthISO 17889.0 Mpa
Flexural modulusISO 1782500 Mpa
Tensile strain屈服ISO 527-210 %
tensile strength 屈服ISO 527-263.0 Mpa
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/F10-05
UL flame retardant rating0.8mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI THAILAND/F10-05
Melt volume flow rate190°C/2.16kgISO 11332.20 cm3/10min
Water absorption rate平衡,23°C,50%RH0.22 %
melt mass-flow rate190°C/2.16kgISO 11332.5 g/10min
Shrinkage rateMD：3.00mm2.2 %
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/F10-05
melting temperatureISO 11357-3166 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B156 °C
1.8MPa,未退火，HDTISO 75-2/A100 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-04 cm/cm/°C
TDISO 11359-21.1E-04 cm/cm/°C