Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS GA-501 NIPPON A&L
KRALASTIC®
chip、Profile、film、Bag
High impact、High toughness
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | NIPPON A&L/GA-501 |
|---|---|---|---|
| melt mass-flow rate | 220℃/10kg | ASTM D-1238 | 32 g/10min |
| density | 23℃ | ASTM D-792 | 1.04 g/cm |
| Mechanical properties | Test Condition | Test Method | NIPPON A&L/GA-501 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 67 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | 23℃ | ASTM D-790 | 2250 Mpa |
| ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | ||
| elongation at break | 23℃ | ASTM D-638 | 20 % |
| bending strength | 23℃ | ASTM D-790 | 62 Mpa |
| tensile strength | 23℃ | ASTM D-638 | 47 Mpa |
| IZOD notch impact strength | 23℃ 6.4mmt | ASTM D-256 | 294 J/m |
| Rockwell hardness | ASTM D785 | 113 | |
| IZOD notch impact strength | -30℃,6.4mmt | ASTM D-256 | 127 J/m |
| Rockwell hardness | 23℃ | ASTM D-785 | 113 R-Scale |
| other | Test Condition | Test Method | NIPPON A&L/GA-501 |
|---|---|---|---|
| 撞击性高 |
| Physical properties | Test Condition | Test Method | NIPPON A&L/GA-501 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.04 |
| physical property | Test Condition | Test Method | NIPPON A&L/GA-501 |
|---|---|---|---|
| Mold shrinkage rate | ASTM D-955 | 0.4-0.6 % |
| Thermal performance | Test Condition | Test Method | NIPPON A&L/GA-501 |
|---|---|---|---|
| mold temperature | 200-260 °C | ||
| UL flame retardant rating | UL94 | HB calss | |
| 1.82Mpa | ASTM D-648 | 85 °C | |
| Combustibility (rate) | UL94 | HB | |
| Ball indentation temperature | 90 °C | ||
| vicat | 1.0kgf | ASTM D-1525 | 105 °C |