Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 770CA30 JILIN JOINATURE
ZYPEEK®
Aerospace、Wire and cable、Automotive sector、Nursing supplies、Medical supplies、Electronic field、Electrical field
Carbon fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JILIN JOINATURE/770CA30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1U | 45 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/U | 45 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179-1eA | 7 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/A | 9 kJ/m² |
| Mechanical properties | Test Condition | Test Method | JILIN JOINATURE/770CA30 |
|---|---|---|---|
| bending strength | 断裂，23℃ | ISO 178 | 380 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 23000 Mpa |
| compressive strength | 23℃ | ISO 604 | 300 Mpa |
| tensile strength | 断裂，23℃ | ISO 527 | 260 Mpa |
| Shore hardness | 23℃ | ISO 868 | 88 D 级 |
| Tensile strain | 断裂，23℃ | ISO 527 | 1.7 % |
| Electrical performance | Test Condition | Test Method | JILIN JOINATURE/770CA30 |
|---|---|---|---|
| Volume resistivity | 23 ℃，1V | IEC 60093 | 10^5 ohms·cm |
| physical property | Test Condition | Test Method | JILIN JOINATURE/770CA30 |
|---|---|---|---|
| density | 结晶 | ISO 1183 | 1.4 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.1 % |
| MD | ISO 294-4 | 0.5 % | |
| Water absorption rate | 23℃，24hr，3.2 mm厚拉伸棒 | ISO 62-1 | 0.04 % |
| melt mass-flow rate | 380℃，5.0kg | ISO 1133 | 2.3 g/10min |
| Water absorption rate | 平衡，23℃ | ISO 62-1 | 0.3 % |
| Thermal performance | Test Condition | Test Method | JILIN JOINATURE/770CA30 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 低于Tg沿着流动方向 | ISO 11359 | 5 ppm/K |
| Heat distortion temperature | 1.8 Mpa，HDT | ISO 75-f | 336 °C |
| thermal conductivity | 23℃ | ISO 22007-4 | 0.95 W/m/K |
| melting temperature | ISO 11357 | 343 °C | |
| Linear coefficient of thermal expansion | 高于Tg沿着流动方向 | ISO 11359 | 6 ppm/K |
| specific heat | 23℃ | DSC | 1.8 kJ/kg /℃ |
| Tg (initial) | ISO 11357 | 143 °C |