ABS PA-757K ZHANGZHOU CHIMEI
POLYLAC®
Automotive Applications、Household daily necessiti、Home appliance components
High rigidity、High gloss、Medium impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-757K |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 21 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 210 J/m |
| 23°C,6.40mm | ASTM D256 | 200 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.0 kJ/m² |
| 23°C | ISO 180/1A | 19 kJ/m² |
| hardness | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-757K |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-757K |
|---|---|---|---|
| bending strength | --5 | ASTM D790 | 80.4 Mpa |
| tensile strength | 屈服4 | ASTM D638 | 45.9 Mpa |
| 屈服 | ISO 527-2/50 | 47.0 Mpa | |
| elongation | 断裂4 | ASTM D638 | 25 % |
| bending strength | --6 | ISO 178 | 76.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 30 % |
| Flexural modulus | --6 | ISO 178 | 2200 Mpa |
| --5 | ASTM D790 | 2620 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 34.0 Mpa |
| flammability | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-757K |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-757K |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.6 g/10min |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| density | --3 | ASTM D792 | 1.05 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 18.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-757K |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
| 1.8MPa,退火，HDT | ASTM D648 | 95.0 °C | |
| vicat | -- | ASTM D15257 | 105 °C |
| -- | ISO 306/A50 | 104 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 98.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 83.0 °C | |
| vicat | -- | ISO 306/B50 | 100 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.6E-05 cm/cm/°C |