Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE Osterlene® LLSH0917 OSTERMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | OSTERMAN USA/Osterlene® LLSH0917 |
|---|---|---|---|
| tensile strength | TD:断裂 | ASTM D882 | 51.0 MPa |
| Thin film puncture strength | 内部方法 | 3.62 J | |
| elongation | MD:断裂 | ASTM D882 | 630 % |
| Dart impact | ASTM D1709A | 330 g | |
| tensile strength | MD:断裂 | ASTM D882 | 62.7 MPa |
| Secant modulus | 1%正割,MD | ASTM D882 | 165 MPa |
| Thin film puncture strength | 内部方法 | 44.5 N | |
| Elmendorf tear strength | MD | ASTM D1922 | 460 g |
| tensile strength | TD:屈服 | ASTM D882 | 9.65 MPa |
| Secant modulus | 1%正割,TD | ASTM D882 | 186 MPa |
| Elmendorf tear strength | TD | ASTM D1922 | 600 g |
| tensile strength | MD:屈服 | ASTM D882 | 8.96 MPa |
| elongation | TD:断裂 | ASTM D882 | 720 % |
| optical performance | Test Condition | Test Method | OSTERMAN USA/Osterlene® LLSH0917 |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 37 |
| Haze ratio | ASTM D1003 | 17 % |
| physical property | Test Condition | Test Method | OSTERMAN USA/Osterlene® LLSH0917 |
|---|---|---|---|
| density | 内部方法 | 0.917 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.90 g/10min |
| Thermal performance | Test Condition | Test Method | OSTERMAN USA/Osterlene® LLSH0917 |
|---|---|---|---|
| melting temperature | 内部方法 | 125 °C |