PC BPL1000-701 SABIC INNOVATIVE US
LEXAN™
Automotive components、Electronic and electrical、Thin walled products
UV resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000-701 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C |
| RTIElec | UL746 | 80.0 °C | |
| Vicat Softening Temperature | ASTMD152511 | 111 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C |
| RTIStr | UL746 | 80.0 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 114 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 96.1 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 113 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 106 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 80.0 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000-701 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 25 g/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 23.2 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.50to0.70 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000-701 |
|---|---|---|---|
| Tensile Stress | 断裂 | ISO527-2/50 | 53.5 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 96 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 97 % |
| Tensile Modulus | ISO527-2/1 | 2460 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 63.4 Mpa |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2670 Mpa |
| ISO178 | 2370 Mpa | ||
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 102 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.8 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 64.8 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.7 % |
| Flexural Strength | ISO178 | 94.8 Mpa | |
| Tensile Modulus | ASTMD638 | 2680 Mpa | |
| Tensile Strength | Break | ASTMD638 | 51.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000-701 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 12 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 48.6 J |
| 23°C | ISO179/1eA | 18 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 18 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000-701 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 800 °C |
| Oxygen Index | ISO4589-2 | 36 % | |
| Flame Rating | 0.8mm | UL94 | V-0 |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Flame Rating | 0.45mm | UL94 | V-2 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000-701 |
|---|---|---|---|
| Dielectric Strength | 1.60mm,inOil | ASTMD149 | 27 KV/mm |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 200 V | |
| Dissipation Factor? | 60Hz | IEC60250 | 0.030 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 60Hz | IEC60250 | 3.00 |
| 1MHz | IEC60250 | 2.90 | |
| Dissipation Factor? | 50Hz | IEC60250 | 0.030 |
| Relative Permittivity | 50Hz | IEC60250 | 3.00 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.010 |