Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3GF10 AKRO-PLASTIC GERMANY
AKROMID®
Industrial applications、Automotive sector、Engineering accessories
high strength、High rigidity、Glass fiber reinforced、enhance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 38 kJ/m² |
| -10°C | ISO 179/1eU | 37 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 10 % |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Surface Resistivity | IEC 60093 | 1E+12 ohms |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 4800 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 115 Mpa |
| bending strength | ISO 178 | 170 Mpa | |
| Flexural modulus | ISO 178 | 4400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.5 % |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 0.60 % | |
| moisture absorption | 70°C，62%RH | ISO 1110 | 2.6to2.8 % |
| spiral flow length | 内部方法 | 102 CM | |
| Water absorption rate | 饱和,23°C | ISO 62 | 7.5to8.0 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF10 |
|---|---|---|---|
| TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC 216 | 130to150 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| melting temperature | DIN EN11357-1 | 262 °C | |
| TemperatureIndex | 50%LossofTensileStrength,5000hr | IEC 216 | 160to175 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 245 °C |