PPO GFN1630V-801 SABIC INNOVATIVE NETHERLANDS

FLEX NORYL™

Automotive components,Laptop case

High temperature resistan,Hydrolysis resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
Rockwell hardness	L-Sale	ASTM D785	104

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	132 °C
		1.8MPa,Unannealed,3.20mm	ASTM D648	122 °C
		1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	124 °C
		1.8MPa,Unannealed,6.40mm	ASTM D648	125 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	131 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	5.1E-05 cm/cm/°C
Linear coefficient of thermal expansion		TD：-40to40°C	ASTME831	7.1E-05 cm/cm/°C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI Str		UL 746	90.0 °C
Vicat softening temperature	--	ISO 306/B120	134 °C
Vicat softening temperature		--	ISO 306/B50	131 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
Bending modulus	50.0mmSpan4	ASTM D790	3840 Mpa
			ISO 178	4160 Mpa
		100mmSpan5	ASTM D790	3590 Mpa
bending strength	Yield,50.0mmSpan4	ASTM D790	116 Mpa
			ISO 178	122 Mpa
		Yield,100mmSpan5	ASTM D790	108 Mpa
elongation	Break	ASTM D638	3.0 %
Tensile modulus		ISO 527-2/1	4400 Mpa
Tensile modulus			ASTM D638	4350 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength	Break	ASTM D638	63.0 Mpa
tensile strength		Break	ISO 527-2	64.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
Arc resistance		ASTM D495	PLC7
Dielectric constant	1MHz	ASTM D150	2.90
Dissipation factor	1MHz	ASTM D150	1.4E-03
High arc combustion index	HAI	UL 746	PLC 4
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 5

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
melt mass-flow rate	300°C/5.0kg	ASTM D1238	17 g/10min
Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	16.4 cm3/10min
Outdoor applicability		UL 746C	f1
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.50 %
Water absorption rate	24hr	ASTM D570	0.060 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
Dart impact	23°C,TotalEnergy	ASTM D3763	21.7 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	9.4 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	11 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	33 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	35 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	28 kJ/m²
Suspended wall beam without notch impact strength		-30°C	ISO 180/1U	25 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE NETHERLANDS/GFN1630V-801
UL flame retardant rating	1.5mm	UL 94	HB