Impact resistance | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 4.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
Suspended wall beam without notch impact strength | ISO 180 | 80 kJ/m² | |
Impact strength of cantilever beam gap | 23°C | ISO 180/A | 6.0 kJ/m² |
hardness | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 60.0 MPa |
Mechanical properties | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
Tensile strain | 断裂,23°C | ISO 527-2 | 50 % |
tensile strength | 屈服,23°C | ISO 527-2 | 28.0 MPa |
Tensile modulus | ISO 527-2 | 2100 MPa | |
Flexural modulus | ISO 178 | 2000 MPa | |
bending strength | ISO 178 | 50.0 MPa |
Electrical performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
dielectric constant | 100Hz | IEC 60250 | 2.50 |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
Surface Resistivity | IEC 60093 | >1.0E+14 ohms |
optical performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
transmissivity | 550nm | ASTM D1003 | 90.0 % |
Haze ratio | ASTM D1003 | 2.0 % | |
refractive index | ISO 489 | 1.570 |
physical property | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 55.0 cm³/10min |
Shrinkage rate | ISO 294-4 | 0.20to0.60 % | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
饱和,23°C | ISO 62 | 0.10 % | |
density | ISO 1183 | 1.05 g/cm³ | |
Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 5.00 cm³/10min |
Thermal performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 550 |
---|---|---|---|
vicat | ASTM D15253 | 99.0 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 70.0 °C |
vicat | ISO 306/B50 | 73.0 °C | |
Heat distortion temperature | 0.45MPa,Annealed,HDT | ISO 75-2/B | 81.0 °C |
maximum service temperature | 250 °C |