Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TP, Unspecified Hapflex™ 560-6 HAPCO USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HAPCO USA/Hapflex™ 560-6 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 无断裂 | |
| Impact strength of cantilever beam gap | ASTM D256 | 无断裂 |
| hardness | Test Condition | Test Method | HAPCO USA/Hapflex™ 560-6 |
|---|---|---|---|
| Shore hardness | 邵氏A | ASTM D2240 | 60 |
| Mechanical properties | Test Condition | Test Method | HAPCO USA/Hapflex™ 560-6 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 600 % |
| tensile strength | ASTM D638 | 8.96 MPa | |
| Tensile modulus | ASTM D638 | 2.96 MPa |
| thermosetting | Test Condition | Test Method | HAPCO USA/Hapflex™ 560-6 |
|---|---|---|---|
| Thermosetting mixed viscosity | 25°C | ASTM D4878 | 2250 cP |
| GelTime | 25°C | ASTM D2971 | 6.0 min |
| stripping time | 21°C | 内部方法 | 60to120 min |
| Thermosetting components | 部件A | 按重量计算的混合比:100.按容量计算的混合比:100 | |
| 部件B | 按重量计算的混合比:55.按容量计算的混合比:50 |
| physical property | Test Condition | Test Method | HAPCO USA/Hapflex™ 560-6 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D2566 | 0.20to0.40 % |
| density | ASTM D4669 | 1.06 g/cm³ | |
| Weight Percubicinch | 17 g |
| elastomer | Test Condition | Test Method | HAPCO USA/Hapflex™ 560-6 |
|---|---|---|---|
| tear strength | ASTM D624 | 15.1 kN/m |