Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 6129 NC010 DuPont, European Union
Crastin®
Electronic and electrical、Automotive Applications、Non specific food applica
Flame retardant、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | DuPont, European Union/6129 NC010 |
|---|---|---|---|
| Tensile creep modulus | 1Hr | ISO 899-1 | 2600 Mpa |
| bending strength | 23°C | ISO 178 | 85.0 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| 23°C | ISO 179/1eA | 5.5 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.5 kJ/m² |
| Tensile creep modulus | 1000Hr | ISO 899-1 | 1800 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2350 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| elongation at break | 23°C | ISO 527-2 | >50 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 58.0 Mpa |
| Electrical performance | Test Condition | Test Method | DuPont, European Union/6129 NC010 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| dielectric strength | IEC 60243-1 | 26 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+12 Ω.cm | |
| Volume resistivity | IEC 60093 | >1.0E+15 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | DuPont, European Union/6129 NC010 |
|---|---|---|---|
| GWIT | 0.92mm | IEC 60695-2-12 | 825 °C |
| 3.00mm | IEC 60695-2-12 | 825 °C | |
| Relative temperature of heating wire | 3.00mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | UL -94 | HB 0.92mm | |
| Relative temperature of heating wire | 0.92mm | IEC 60695-2-13 | 925 °C |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| Relative temperature of heating wire | 1.50mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm | ||
| GWIT | 1.50mm | IEC 60695-2-12 | 825 °C |
| physical property | Test Condition | Test Method | DuPont, European Union/6129 NC010 |
|---|---|---|---|
| Shrinkage rate | MD2.0mm | ISO 294-4 | 1.5 % |
| density | ISO 1183 | 1.30 g/cm³ | |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 1.7 % |
| Thermal performance | Test Condition | Test Method | DuPont, European Union/6129 NC010 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 50.0 °C |
| vicat | ISO 306/B50 | 175 °C | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/A | 60.0 °C |
| vicat | 熔融温度 | ISO 11357-3 | 225 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 115 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa退火，HDT | ISO 75-2/B | 180 °C |