Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS POLYabs F20 UV4 POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYabs F20 UV4 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 16 kJ/m² |
| -20°C | ISO 179 | 11 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/POLYabs F20 UV4 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2300 MPa |
| tensile strength | ISO 527-2 | 43.0 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.5 % |
| bending strength | ISO 178 | 78.0 MPa |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/POLYabs F20 UV4 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/POLYabs F20 UV4 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60to0.80 % |
| MD | ISO 294-4 | 0.60to0.80 % | |
| density | ISO 1183 | 1.04 g/cm³ | |
| melt mass-flow rate | 230°C/5.0kg | ISO 1133 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYabs F20 UV4 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 87.0 °C |
| vicat | -- | ISO 306/A50 | 106 °C |
| -- | ISO 306/B50 | 100 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 76.0 °C |