Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SPS S136 IDEMITSU JAPAN
XAREC™
Electrical applications、Household daily necessiti
Glass fiber reinforced、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/S136 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃23℃ | ISO 180 | 9 kJ/m² |
| Charpy Notched Impact Strength | 23℃23℃ | ISO 179 | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23℃23℃ | ISO 179 | 28 kJ/m² |
| Suspended wall beam without notch impact strength | 23℃23℃ | ISO 180 | 29 kJ/m² |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/S136 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10600 Mpa | |
| tensile strength | 断裂断裂 | ISO 527-2 | 115 Mpa |
| bending strength | ISO 178 | 170 Mpa | |
| Tensile strain | 断裂断裂 | ISO 527-2 | 1.6 % |
| Flexural modulus | ISO 178 | 10000 Mpa |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/S136 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | ASTM D149 | 35 KV/mm | |
| Dissipation Factor | 1 MHz1 MHz | IEC 60250 | 0.002 |
| Volume resistivity | IEC 60093 | > 1.0E+16 ohms·cm | |
| dielectric constant | 1 MHz1 MHz | IEC 60250 | 3 |
| arc resistance | ASTM D495 | PLC 6 |
| Flame retardant performance | Test Condition | Test Method | IDEMITSU JAPAN/S136 |
|---|---|---|---|
| > 1.50 mm> 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/S136 |
|---|---|---|---|
| Shrinkage rate | MDFlow | 内部方法 | 0.10 - 0.40 % |
| Water absorption rate | 平衡，23℃，50% RH平衡，23℃，50% RH2 | ISO 62 | 0.02 % |
| density | ISO 1183 | 1.42 g/cm³ | |
| Shrinkage rate | TDAcross Flow | 内部方法 | 0.50 - 0.80 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/S136 |
|---|---|---|---|
| Relative Heat Index (RTI) | 强度机械性能 | UL 746 | 50 °C |
| Linear coefficient of thermal expansion | MD：-30~30℃MD：-30 到 30℃ | TMA | 0.000020 1/℃ |
| Heat distortion temperature | 0.45 MPa，未退火，HDT | ISO 75-2/B | 265 °C |
| 1.8 MPa，未退火1.8 MPa，未退火，HDT | ISO 75-2/A | 245 °C | |
| Relative Heat Index (RTI) | 电气性能 | UL 746 | 50 °C |
| Linear coefficient of thermal expansion | TD：-30~30℃TD：-30 到 30℃ | TMA | 0.000040 1/℃ |
| Relative Heat Index (RTI) | 冲击机械性能 | UL 746 | 50 °C |