PPO GX1050 MITSUBISHI ENGINEERING JAPAN
IUPIACE™
Electronic and electrical、lighting
Flame retardant grade、Glass fiber reinforced、Low Specific Gravity、Stable forming size、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GX1050 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.7 % |
| bending strength | 23°C | ISO 178 | 122 Mpa |
| Flexural modulus | 23°C | ISO 178 | 6000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 6100 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 75.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GX1050 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 5E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GX1050 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | 5VB |
| 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GX1050 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.30-0.50 % | |
| MD:3.20mm | 0.20-0.40 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.060 % |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 24.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GX1050 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.8E-05 cm/cm/°C |