Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE NOVAPOL® PF-Y821-MPR NOVA Chemicals
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | NOVA Chemicals/NOVAPOL® PF-Y821-MPR |
|---|---|---|---|
| Low friction puncture | 38.0µm | 内部方法 | 320 J/cm |
| film | Test Condition | Test Method | NOVA Chemicals/NOVAPOL® PF-Y821-MPR |
|---|---|---|---|
| tensile strength | MD:屈服,38µm,吹塑薄膜 | ASTM D882 | 10.0 MPa |
| Secant modulus | 1%正割,TD:38µm,吹塑薄膜 | ASTM D882 | 230 MPa |
| elongation | MD:断裂,38µm,吹塑薄膜 | ASTM D882 | 660 % |
| tensile strength | MD:断裂,38µm,吹塑薄膜 | ASTM D882 | 30.0 MPa |
| film thickness | 38 µm | ||
| Elmendorf tear strength | TD:38µm,吹塑薄膜 | ASTM D1922 | 390 g |
| tensile strength | TD:屈服,38µm,吹塑薄膜 | ASTM D882 | 10.0 MPa |
| elongation | TD:断裂,38µm,吹塑薄膜 | ASTM D882 | 730 % |
| Dart impact | 38µm,吹塑薄膜 | ASTM D1709A | 140 g |
| Elmendorf tear strength | MD:38µm,吹塑薄膜 | ASTM D1922 | 200 g |
| tensile strength | TD:断裂,38µm,吹塑薄膜 | ASTM D882 | 25.0 MPa |
| Secant modulus | 1%正割,MD:38µm,吹塑薄膜 | ASTM D882 | 190 MPa |
| Mechanical properties | Test Condition | Test Method | NOVA Chemicals/NOVAPOL® PF-Y821-MPR |
|---|---|---|---|
| coefficient of friction | 吹塑薄膜 | ASTM D1894 | >0.50 |
| optical performance | Test Condition | Test Method | NOVA Chemicals/NOVAPOL® PF-Y821-MPR |
|---|---|---|---|
| gloss | 45°,38.0µm,吹塑薄膜 | ASTM D2457 | 57 |
| Haze ratio | 38.0µm,吹塑薄膜 | ASTM D1003 | 11 % |
| physical property | Test Condition | Test Method | NOVA Chemicals/NOVAPOL® PF-Y821-MPR |
|---|---|---|---|
| density | ASTM D792 | 0.923 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |