PA6 Niretan B C35 Soredi S.p.a.
--
--
Filler, Soredi, Soredi, Italy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C,3.20mm | J/m | 40 60 |
-20°C,3.20mm | J/m | 30 30 |
hardness | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
Rockwell hardness | R级 | 90 40 |
Electrical performance | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
Surface Resistivity | ohms | 1E+14 1E+13 | |
Volume resistivity | ohms·cm | 1E+15 1E+12 | |
dielectric strength | 1.00mm | kV/mm | 30 25 |
relative permittivity | 1MHz | 3.50 4.00 | |
Dissipation Factor | 1MHz | 0.020 0.10 |
Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
Flexural modulus | MPa | 700 2500 | |
tensile strength | 屈服 | MPa | 70.0 40.0 |
elongation | 断裂 | % | 3.0 30 |
bending strength | 断裂 | MPa | 120 50.0 |
flammability | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
UL flame retardant rating | 1.60mm | HB -- | |
Hot filament ignition temperature | 2.00mm | °C | 650 -- |
UL flame retardant rating | 3.20mm | HB -- |
physical property | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
density | g/cm³ | 1.40 -- | |
Shrinkage rate | MD | % | 0.60 1.2 |
Water absorption rate | 平衡,23°C,50%RH | % | 2.0 -- |
23°C,24hr | % | 5.0 6.0 |
Thermal performance | Test Condition | Test Method | Soredi S.p.a./Niretan B C35 |
---|---|---|---|
Linear coefficient of thermal expansion | MD:23到55°C | cm/cm/°C | 6E-05 -- |
Heat distortion temperature | 1.8MPa,未退火,HDT | °C | 120 -- |
Crystallization peak temperature | DSC | °C | 220 -- |