PC/ABS FR3050 012305 COVESTRO THAILAND
Bayblend® 
Automotive components,Electronic and electrical components
High temperature resistan,Non enhanced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodCOVESTRO THAILAND/FR3050 012305
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B126 °C
1.8MPa,UnannealedISO 75-2/A115 °C
Linear coefficient of thermal expansionMD:23to55°CISO 11359-26.8E-05 cm/cm/°C
TD:23to55°CISO 11359-26.8E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B120136 °C
--ISO 306/B50134 °C
mechanical propertiesTest ConditionTest MethodCOVESTRO THAILAND/FR3050 012305
Tensile modulus23°CISO 527-2/12400 Mpa
Tensile strainYield,23°CISO 527-2/505.0 %
Break,23°CISO 527-2/50>50 %
tensile strengthBreak,23°CISO 527-2/5060.0 Mpa
Yield,23°CISO 527-2/5065.0 Mpa
Electrical performanceTest ConditionTest MethodCOVESTRO THAILAND/FR3050 012305
Compared to the anti leakage trace indexSolutionAIEC 60112 V
Dielectric strength23°C,1.00mmIEC 60243-135 KV/mm
Dissipation factor23°C,100HzIEC 602502E-03
23°C,1MHzIEC 602508E-03
Relative permittivity23°C,1MHzIEC 602503.10
23°C,100HzIEC 602503.20
Surface resistivityIEC 600931E+17 ohms
Volume resistivity23°CIEC 600931E+17 ohms·cm
Physical propertiesTest ConditionTest MethodCOVESTRO THAILAND/FR3050 012305
MeltViscosity260°CISO 11443-A480 Pa·s
Melt Volume Flow Rate (MVR)260°C/5.0kgISO 113318.0 cm3/10min
Shrinkage rateMD:260°C,3.00mmISO 25770.50-0.70 %
TD:260°C,3.00mmISO 25770.50-0.70 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.20 %
Saturation,23°CISO 620.50 %
impact performanceTest ConditionTest MethodCOVESTRO THAILAND/FR3050 012305
Suspended wall beam without notch impact strength23°CISO 180NoBreak
flammabilityTest ConditionTest MethodCOVESTRO THAILAND/FR3050 012305
UL flame retardant rating3.0mmUL 945VA
2.0mmUL 945VB
1.0mmUL 94V-1
1.5mmUL 94V-0