ABS 3001MG2A UMG JAPAN
UMG ABS®
Automotive components
Flame retardant,High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 107 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| melt mass-flow rate | 24 g/10min |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| Charpy Notched Impact Strength | 31 kJ/m² | ||
| Flexural modulus | ASTM D790/ISO 178 | 2.400 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23°C | ISO 178 | 65.0 Mpa |
| Flexural modulus | 2400 Mpa | ||
| 23°C | ISO 178 | 2300 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 2200 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 31 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 23°C | ISO 527-2 | 41.0 Mpa |
| other | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| characteristic | 电镀.涂饰 |
| Physical properties | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 24 g/10min |
| physical property | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 24.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/3001MG2A |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 80.0 °C |
| HDT | 80 °C | ||
| HDT | ASTM D648/ISO 75 | 80 ℃（℉） | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |