PA WINDFORM® XT 2.0 CRP Technology s.r.l.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CRP Technology s.r.l./WINDFORM® XT 2.0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.7 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 19 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 5.3 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 22 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CRP Technology s.r.l./WINDFORM® XT 2.0 |
|---|---|---|---|
| Flexural modulus | perdensityunit | 6690 MPa/g/cm³ | |
| tensile strength | ISO 527-2 | 83.8 MPa | |
| Tensile modulus | ISO 527-2 | 8930 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.8 % |
| UltimateTensileStrength | 76.4 MPa/g/cm³ | ||
| FlexuralStrength | 121 MPa/g/cm³ | ||
| Flexural modulus | ISO 178 | 7340 MPa | |
| Tensile modulus | 8140 MPa/g/cm³ | ||
| bending strength | ISO 178 | 133 MPa |
| Electrical performance | Test Condition | Test Method | CRP Technology s.r.l./WINDFORM® XT 2.0 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | <1.0E+8 ohms·cm | |
| Surface Resistivity | ASTM D257 | <1.0E+8 ohms |
| physical property | Test Condition | Test Method | CRP Technology s.r.l./WINDFORM® XT 2.0 |
|---|---|---|---|
| density | 20°C | 1.10 g/cm³ |
| Thermal performance | Test Condition | Test Method | CRP Technology s.r.l./WINDFORM® XT 2.0 |
|---|---|---|---|
| vicat | ISO 306/A50 | 176 °C | |
| melting temperature | ISO 11357 | 179 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 173 °C |