Certificates
POM LZ750 ASAHIKASEI SUZHOU
TENAC™-C
Engine parts、Household goods、Engineering accessories、Shell、Outdoor applications
Low friction coefficient、Homopolymer、wear resistant、Lubricity、Low viscosity、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHIKASEI SUZHOU/LZ750 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 86 |
| R级 | ASTM D785 | 117 |
| Mechanical properties | Test Condition | Test Method | ASAHIKASEI SUZHOU/LZ750 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2700 Mpa | |
| elongation | 断裂 | ASTM D638 | 20 % |
| tensile strength | -- | ASTM D638 | 60.0 Mpa |
| bending strength | ASTM D790 | 91.0 Mpa | |
| Flexural modulus | -- | ISO 178 | 2700 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| Flexural modulus | -- | ASTM D790 | 2800 Mpa |
| elongation | 断裂 | ISO 527-2 | 15 % |
| flammability | Test Condition | Test Method | ASAHIKASEI SUZHOU/LZ750 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHIKASEI SUZHOU/LZ750 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.6-2.0 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 30 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHIKASEI SUZHOU/LZ750 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 100 °C |
| 0.45MPa,未退火，HDT | ASTMD648 | 157 °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |