PC GSH2010PH-98TTEA MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Automotive Applications、electrical equipment、Phone
Glass fiber reinforced、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010PH-98TTEA
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010PH-98TTEA
Tensile modulusISO 527-22900 Mpa
Nominal tensile fracture strainISO 527-210 %
bending strengthISO 17890.0 Mpa
Flexural modulusISO 1782700 Mpa
Tensile strain屈服ISO 527-25.0 %
tensile strength 屈服ISO 527-252.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010PH-98TTEA
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010PH-98TTEA
UL flame retardant rating0.40mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010PH-98TTEA
Shrinkage rateTD:3.20mm0.30-0.50 %
Melt volume flow rate300°C/1.2kgISO 113314.0 cm3/10min
Shrinkage rate吸水率(饱和,23°C)0.14 %
MD:3.20mm0.30-0.50 %
melt mass-flow rate300°C/1.2kgISO 113315 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010PH-98TTEA
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B132 °C
1.8MPa,未退火，HDTISO 75-2/A125 °C
Linear coefficient of thermal expansionMDISO 11359-25.8E-05 cm/cm/°C
TDISO 11359-25.8E-05 cm/cm/°C