Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CX7240-7M7D037 SABIC INNOVATIVE US
CYCOLAC™
Electrical field、Electronic field、Architectural application、Outdoor applications、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Casters、Aerospace Applications、Liquid handling
Flame retardant、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| RTI | UL 746 | 90.0 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 99.0 °C |
| Thermal Conductivity | ISO 8302 | 0.20 W/m/K | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10 | ISO 75-2/Af | 93.0 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO 306/B120 | 113 °C |
| RTI Elec | UL 746 | 90.0 °C | |
| Vicat Softening Temperature | -- | ASTM D152511, ISO 306/B5011 | 110 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 7.5E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 90.0 °C | |
| Ball PressureTest | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 89.0 °C |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 100 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| Suggested Max Moisture | 0.020 % | ||
| Middle Temperature | 240 到 290 °C | ||
| Processing (Melt) Temp | 250 到 300 °C | ||
| Drying Time | 2.0 到 4.0 hr | ||
| Rear Temperature | 230 到 280 °C | ||
| Nozzle Temperature | 250 到 300 °C | ||
| Drying Temperature | 80 到 90 °C | ||
| Front Temperature | 250 到 300 °C | ||
| Hopper Temperature | 60 到 80 °C | ||
| Mold Temperature | 60 到 85 °C | ||
| Vent Depth | 0.030 到 0.075 mm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/2.16 kg | ASTM D1238 | 18 g/10 min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.40 到 0.60 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.20 % |
| Melt Volume flow Rate | 260°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2600 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 100 % |
| Tensile Strength | 屈服 3 | ASTM D638 | 65.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2500 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 2600 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 104 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 4.1 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 96.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2500 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 90 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 58.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| Glow Wire Flammability Index | 0.75 mm 13 | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| Glow Wire Flammability Index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 0.75 mm 13 | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 |
| 3.0 mm | UL 94 | 5VA | |
| Glow Wire Ignition Temperature | 1.5 mm 13 | IEC 60695-2-13 | 775 °C |
| Oxygen Index | ISO 4589-2 | 34 % | |
| Glow Wire Ignition Temperature | 3.0 mm 13 | IEC 60695-2-13 | 775 °C |
| 3.0 mm | IEC 60695-2-13 | 800 °C | |
| UL flame retardant rating | 1.5 mm | UL 94 | 5VB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX7240-7M7D037 |
|---|---|---|---|
| Dielectric Strength | 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm |
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Dielectric Strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Dielectric Strength | 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |