Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 2002 JAPAN POLYPLASTIC
DURANEX®
Electrical field、Electronic field
Flame retardant、Good flexibility、Glass fiber reinforced、Friction resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eU | 190 kJ/m² |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 85 |
| M计秤 | ISO 2039-2 | 78 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 34 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 85 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ISO 527-1/-2 | 57 Mpa | |
| bending strength | ASTM D-790 | 85 Mpa | |
| 80°C | 80℃ | ASTM D638 | 469 Mpa |
| elongation | ASTM D-638 | >200 % | |
| elongation at break | ASTM D638/ISO 527 | >200 % | |
| tensile strength | ISO 527-2 | 57.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 3.2 kJ/m² | |
| Yield, 121 ° C | ASTM D638 | 23 % | |
| Flexural modulus | ISO 178 | 3100 Mpa | |
| 23°C | ISO 178 | 2500 Mpa | |
| fracture | ISO 527-2/1A/50 | 220 % | |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | >50 % | |
| 50% strain | 50%应变 | ISO 527-2/1A/50 | 30.0 Mpa |
| 121°C | 121℃ | ASTM D638 | 296 Mpa |
| Surrender, 23 ° C | ASTM D638 | 3.2 % | |
| Flexural modulus | ASTM D790/ISO 178 | 2540 kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 2540 Mpa | ||
| 23°C | ASTM D638 | 3170 Mpa | |
| -40°C | -40℃ | ASTM D638 | 3100 Mpa |
| Yield, 121 ° C | ASTM D638 | 17.9 Mpa | |
| tensile strength | ASTM D-638 | 51 Mpa | |
| yield | ISO 527-2/1A/50 | 60.0 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 51 kg/cm²(MPa)[Lb/in²] | |
| Nominal tensile fracture strain | ISO 527-2 | 12 % | |
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
| Yield, 0 ° C | 屈服,0°C | ASTM D638 | 4.4 % |
| bending strength | ISO 178 | 95 Mpa | |
| Yield, -40 ° C | ASTM D638 | 7.2 % | |
| Yield, 80 ° C | ASTM D638 | 17 % | |
| Surrender, 23 ° C | ASTM D638 | 55.8 Mpa | |
| Yield, 80 ° C | ASTM D638 | 24.8 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 34 J/m | |
| Yield, 0 ° C | 屈服,0°C | ASTM D638 | 75.8 Mpa |
| fracture | ISO 527-2/1A/50 | 35.0 Mpa | |
| Yield, -40 ° C | ASTM D638 | 101 Mpa | |
| Fracture, 23 ° C | ASTM D638 | 200 % | |
| yield | ISO 527-2/1A/50 | 4.0 % |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| 1MHz | 1MHz | IEC 60250 | 3.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 1.4E-03 |
| 1MHz | 1MHz | ASTM D150 | 3.20 |
| 100Hz | 100Hz | IEC 60250 | 4.00 |
| dielectric strength | 3.00mm | IEC 60243-1 | 17 KV/mm |
| --1 | ASTM D149 | 17 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.022 |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 792 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| UL flame retardant rating | 0.710mm | UL 94 | HB |
| UL 94 | HB | ||
| Limiting Oxygen Index | ISO 4589-2 | 22 % |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| Vertical flow direction | ISO 294-4 | 1.8to2.0 % | |
| 流动方向 | ISO 294-4 | 1.8to2.0 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| 平衡,23°C,50%RH | ISO 62 | 0.19 % | |
| melt mass-flow rate | ASTM D1238 | 20 g/10min | |
| flow | ASTM D955 | 1.8to2.0 % | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 18.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2002 |
|---|---|---|---|
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 80 °C |
| 0.45MPa, Not annealed | ASTM D648 | 160 °C | |
| vicat | ISO 306/B50 | 190 °C | |
| 0.45MPa, Not annealed | ISO 75-2/B | 150 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| melting temperature | ISO 11357-3 | 225 °C | |
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 9E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 70 ℃（℉） |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C | |
| 1.8MPa, Not annealed | ASTMD648 | 55.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.4E-04 cm/cm/°C | |
| Heat distortion temperature | 1.82Mpa，HDT | ASTM D-648 | 70 °C |
| UL flame retardant rating | UL 94 | HB |