Product Name / Manufacturer / Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

PC/PBT
PC/PBT SABIC INNOVATIVE US VX5022-1001
Injection grade
US$ 2,730 / MT
FOB Guangzhou port, China
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Linear coefficient of thermal expansionFlow : 23 to 60°CISO 11359-24.0E-5 cm/cm/°C
Across Flow : 23 to 150°CISO 11359-21.1E-4 cm/cm/°C
Flow : 23 to 150°CISO 11359-22.4E-5 cm/cm/°C
Across Flow : -40 to 40°CASTM E8311.0E-4 cm/cm/°C
Across Flow : 23 to 60°CISO 11359-21.0E-4 cm/cm/°C
Vicat softening temperature--ASTM D152511200 °C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-26.9E-5 cm/cm/°C
Flow : -40 to 40°CISO 11359-22.5E-5 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10ISO 75-2/Af120 °C
0.45 MPa, Unannealed, 3.20 mmASTM D648180 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8314.0E-5 cm/cm/°C
Vicat softening temperature--ASTM D152512145 °C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-24.0E-5 cm/cm/°C
Across Flow : 23 to 80°CISO 11359-21.0E-4 cm/cm/°C
Hot deformation temperature0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span10ISO 75-2/Bf180 °C
1.8 MPa, Unannealed, 3.20 mmASTM D648120 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Dielectric strength1.60 mm, in OilASTM D14928 KV/mm
0.800 mm, in OilIEC 60243-131 KV/mm
Compared to the anti leakage trace indexSolution BIEC 60112PLC 4
Dissipation factor1 MHzASTM D1500.014
Dielectric strength3.20 mm, in OilIEC 60243-116 KV/mm
Dielectric constant60 HzIEC 602503.10
Surface resistivityIEC 60093> 1.0E+16 ohms
Dielectric constant50 HzIEC 602503.10
1 MHzASTM D1503.30
Volume resistivity--IEC 60093> 1.0E+16 ohms·cm
Dielectric strength1.60 mm, in OilIEC 60243-128 KV/mm
Dissipation factor50 HzIEC 602501.0E-3
Volume resistivity--ASTM D257> 1.0E+15 ohms·cm
Dielectric strength3.20 mm, in OilASTM D14916 KV/mm
High arc combustion indexUL 746PLC 0
Hot wire ignitionUL 746PLC 0
Dissipation factor60 HzIEC 602501.0E-3
Dielectric strength0.800 mm, in OilASTM D14931 KV/mm
Dielectric constant100 HzIEC 602503.30
Dissipation factor100 HzIEC 602501.0E-3
Compared to the anti leakage trace index--IEC 60112PLC 2
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Shrinkage rateAcross FlowFlow 2Internal Method0.50 - 0.90 %
Water absorption rateSaturation, 23°CISO 620.10 %
melt mass-flow rate266°C/5.0 kgASTM D123850 g/10 min
Melt Volume Flow Rate (MVR)250°C/2.16 kgISO 113313.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.30 - 0.50 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.060 %
Shrinkage rateFlow 2Internal Method0.30 - 0.80 %
Melt Volume Flow Rate (MVR)265°C/5.0 kgISO 113340.0 cm3/10min
melt mass-flow rate265°C/5.0 kgASTM D123850 g/10 min
Melt Volume Flow Rate (MVR)250°C/5.0 kgISO 113328.0 cm3/10min
melt mass-flow rate250°C/2.16 kgASTM D123816 g/10 min
injectionTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Temperature at the front of the material cylinder245 to 265 °C
Mold temperature40 to 100 °C
Processing (melt) temperature250 to 270 °C
Suggested maximum moisture content0.020 %
Spray nozzle temperature240 to 260 °C
drying temperature110 to 120 °C
Temperature in the middle of the barrel240 to 255 °C
drying time2.0 to 4.0 hr
Hopper temperature40 to 60 °C
Temperature at the rear of the barrel230 to 245 °C
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Melt viscosity260°C, 1500 sec^-1ISO 11443215 Pa·s
Filling materialASTM D15251220 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Impact strength of simply supported beam without notch23°C9ISO 179/1eU40 kJ/m²
Suspended wall beam without notch impact strength-30°C10ISO 180/1U35 kJ/m²
23°CASTM D4812650 J/m
23°C10ISO 180/1U40 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/2U55 kJ/m²
-30°CISO 179/2U50 kJ/m²
Dart impact23°C, Total EnergyASTM D376365.0 J
Suspended wall beam without notch impact strength-30°CASTM D4812650 J/m
Impact strength of simply supported beam without notch-30°C9ISO 179/1eU40 kJ/m²
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Extreme Oxygen IndexISO 4589-223 %
UL flame retardant rating3.0 mmUL 94HB
Burning wire flammability index1.0 mmIEC 60695-2-12750 °C
UL flame retardant rating1.5 mmUL 94HB
Burning wire flammability index2.0 mmIEC 60695-2-12850 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
elongationBreakISO 527-2/53.0 %
Bending modulus50.0 mm Span5ASTM D7905800 Mpa
bending strengthYield, 50.0 mm Span5ASTM D790145 Mpa
tensile strengthYieldISO 527-2/5110 Mpa
Bending strain - at breakISO 1783.0 %
elongationYield4ASTM D6383.0 %
Break4ASTM D6383.0 %
tensile strengthBreakISO 527-2/5110 Mpa
bending strength--6,7ISO 178150 Mpa
tensile strengthYield4ASTM D638125 Mpa
Tensile modulus--3ASTM D6387300 Mpa
elongationYieldISO 527-2/53.0 %
Tensile modulus--ISO 527-2/17100 Mpa
Bending modulus--6ISO 1786300 Mpa
tensile strengthBreak4ASTM D638125 Mpa
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/VX5022-1001
Rockwell hardnessR -SaleISO 2039-2122
Ball Pressure TestH 358/30ISO 2039-1205 Mpa

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China