Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT VX5022-1001 SABIC INNOVATIVE US
XENOY™
engineering application 、Automotive components、Electronic and electrical
High mobility、High crystallinity、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C9 | ISO 179/1eU | 40 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 650 J/m |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Suspended wall beam without notch impact strength | -30°C10 | ISO 180/1U | 35 kJ/m² |
| -30°C | ASTM D4812 | 650 J/m | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 55 kJ/m² |
| -30°C | ISO 179/2U | 50 kJ/m² | |
| 23°C9 | ISO 179/1eU | 40 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C10 | ISO 180/1U | 40 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 122 |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 205 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 125 Mpa |
| 断裂 | ISO 527-2/5 | 110 Mpa | |
| elongation | 断裂4 | ASTM D638 | 3.0 % |
| Tensile modulus | --3 | ASTM D638 | 7300 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 5800 Mpa |
| Bending strain - at break | ISO 178 | 3.0 % | |
| bending strength | --6,7 | ISO 178 | 150 Mpa |
| Flexural modulus | --6 | ISO 178 | 6300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 145 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 3.0 % |
| tensile strength | 屈服 | ISO 527-2/5 | 110 Mpa |
| elongation | 屈服4 | ASTM D638 | 3.0 % |
| tensile strength | 断裂4 | ASTM D638 | 125 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 7100 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 3.0 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 28 KV/mm |
| Volume resistivity | -- | ASTM D257 | > 1.0E+15 ohms·cm |
| dielectric strength | 0.800 mm, 在油中 | IEC 60243-1 | 31 KV/mm |
| dielectric constant | 50 Hz | IEC 60250 | 3.10 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 B | IEC 60112 | PLC 4 |
| dielectric strength | 0.800 mm, in Oil | ASTM D149 | 31 KV/mm |
| dielectric constant | 1 MHz | ASTM D150 | 3.30 |
| Dissipation Factor | 100 Hz | IEC 60250 | 1.0E-3 |
| 50 Hz | IEC 60250 | 1.0E-3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| dielectric constant | 100 Hz | IEC 60250 | 3.30 |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 2 |
| dielectric strength | 3.20 mm, in Oil | ASTM D149 | 16 KV/mm |
| 1.60 mm, 在油中 | IEC 60243-1 | 28 KV/mm | |
| dielectric constant | 60 Hz | IEC 60250 | 3.10 |
| Volume resistivity | -- | IEC 60093 | > 1.0E+16 ohms·cm |
| Dissipation Factor | 60 Hz | IEC 60250 | 1.0E-3 |
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| Surface Resistivity | IEC 60093 | > 1.0E+16 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 16 KV/mm |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.014 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB |
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | ISO 4589-2 | 23 % |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| filler | ASTM D152512 | 20 % | |
| melt viscosity | 260°C, 1500 sec^-1 | ISO 11443 | 215 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16 kg | ASTM D1238 | 16 g/10 min |
| 265°C/5.0 kg | ASTM D1238 | 50 g/10 min | |
| Melt volume flow rate | 265°C/5.0 kg | ISO 1133 | 40.0 cm3/10min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.060 % |
| Shrinkage rate | 流动 2 | 内部方法 | 0.30 - 0.80 % |
| 横向流动 2 | 内部方法 | 0.50 - 0.90 % | |
| melt mass-flow rate | 266°C/5.0 kg | ASTM D1238 | 50 g/10 min |
| Melt volume flow rate | 250°C/5.0 kg | ISO 1133 | 28.0 cm3/10min |
| 250°C/2.16 kg | ISO 1133 | 13.0 cm3/10min | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.30 - 0.50 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 4.0E-5 cm/cm/°C |
| vicat | -- | ASTM D152511 | 200 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| 流动 : 23 到 60°C | ISO 11359-2 | 4.0E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10，HDT | ISO 75-2/Bf | 180 °C |
| Linear coefficient of thermal expansion | 流动 : 23 到 80°C | ISO 11359-2 | 4.0E-5 cm/cm/°C |
| 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 6.9E-5 cm/cm/°C | |
| 流动 : 23 到 150°C | ISO 11359-2 | 2.4E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 180 °C |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| vicat | -- | ASTM D152512 | 145 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 1.0E-4 cm/cm/°C | |
| 横向 : 23 到 150°C | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 120 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10，HDT | ISO 75-2/Af | 120 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/VX5022-1001 |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 240 to 255 °C | ||
| Temperature at the rear of the barrel | 230 to 245 °C | ||
| Processing (melt) temperature | 250 to 270 °C | ||
| Hopper temperature | 40 to 60 °C | ||
| drying temperature | 110 to 120 °C | ||
| Temperature at the front of the material cylinder | 245 to 265 °C | ||
| Temperature | 40 to 100 °C | ||
| Spray nozzle temperature | 240 to 260 °C |