Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 1013NW8 UBE JAPAN
UBE
--
Low viscosity、Fast forming cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | UBE JAPAN/1013NW8 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 1100 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 28500 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 8 % | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 6.5 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 100 % | |
| tensile strength | ASTM D638/ISO 527 | 800 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | UBE JAPAN/1013NW8 |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.5 | |
| Volume resistivity | ASTM D257/IEC 60093 | 10 Ω.cm |
| other | Test Condition | Test Method | UBE JAPAN/1013NW8 |
|---|---|---|---|
| characteristic | 阻燃性 |
| Physical properties | Test Condition | Test Method | UBE JAPAN/1013NW8 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.14 | |
| Water absorption rate | ASTM D570/ISO 62 | 10.7 % |
| Thermal performance | Test Condition | Test Method | UBE JAPAN/1013NW8 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 75 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 8 mm/mm.℃ |