EPE ELITE™ 5940G DOW USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW USA/ELITE™ 5940G |
|---|---|---|---|
| film strength | MD | ASTM D882 | 108 J/cm³ |
| tensile strength | TD:断裂 | ASTM D882 | 32.4 MPa |
| elongation | MD:断裂 | ASTM D882 | 460 % |
| Dart impact | ASTM D1709A | 120 g | |
| tensile strength | MD:断裂 | ASTM D882 | 35.9 MPa |
| Thin film puncture strength | 内部方法 | 9.51 J/cm³ | |
| 44.5 N | |||
| Secant modulus | 2%正割,TD | ASTM D882 | 607 MPa |
| 1%正割,MD | ASTM D882 | 625 MPa | |
| Thin film puncture strength | 1.92 J | ||
| Elmendorf tear strength | MD | ASTM D1922 | 40 g |
| Secant modulus | 2%正割,MD | ASTM D882 | 503 MPa |
| tensile strength | TD:屈服 | ASTM D882 | 24.1 MPa |
| Secant modulus | 1%正割,TD | ASTM D882 | 758 MPa |
| film thickness | 25 µm | ||
| Elmendorf tear strength | TD | ASTM D1922 | 650 g |
| film strength | TD | ASTM D882 | 124 J/cm³ |
| tensile strength | MD:屈服 | ASTM D882 | 20.7 MPa |
| elongation | TD:断裂 | ASTM D882 | 640 % |
| optical performance | Test Condition | Test Method | DOW USA/ELITE™ 5940G |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 20 |
| Haze ratio | ASTM D1003 | 30 % |
| physical property | Test Condition | Test Method | DOW USA/ELITE™ 5940G |
|---|---|---|---|
| density | ASTM D792 | 0.940 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.85 g/10min |
| Thermal performance | Test Condition | Test Method | DOW USA/ELITE™ 5940G |
|---|---|---|---|
| vicat | ASTM D1525 | 122 °C | |
| melting temperature | 内部方法 | 126 °C |