PA66 D5G3BM BK20560 BASF GERMANY
Ultramid®
Industrial machinery,Electrical applications
Oil resistant,High mobility,Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/D5G3BM BK20560 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 48 kJ/m² |
| 23°C | ISO 179 | 84 kJ/m² |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/D5G3BM BK20560 |
|---|---|---|---|
| Inflation ratio (BUR) | 2.0:1.0 | ||
| Blow molding drying temperature | 71 °C | ||
| Blow molding mold temperature | 60to90 °C | ||
| Blow molding melt temperature | 270to290 °C | ||
| Blow molding drying time | 2.0to4.0 hr | ||
| BlowMoldingMoistureContent | 0.15 % |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/D5G3BM BK20560 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 5.0 % |
| tensile strength | 断裂,150°C | ISO 527-2 | 46.0 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2 | 17 % |
| Tensile modulus | 23°C | ISO 527-2 | 5500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 115 Mpa |
| Tensile modulus | 150°C | ISO 527-2 | 1700 Mpa |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/D5G3BM BK20560 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 250 °C |
| Linear coefficient of thermal expansion | MD | 3.3E-5to3.4E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 220 °C |
| Linear coefficient of thermal expansion | TD | 9.5E-5to1.3E-4 cm/cm/°C | |
| melting temperature | ISO 3146 | 260 °C |