PC/ABS XCY620H SABIC INNOVATIVE US
CYCOLAC™
Home appliance components、Electrical applications
High mobility、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 55.0 J |
| -30°C,TotalEnergy | ASTM D3763 | 65.0 J | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 40 kJ/m² |
| 23°C | ISO 180/1A | 55 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 39 KV/mm |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+16 ohms |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2200 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 54.0 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 86.0 Mpa |
| ISO 178 | 82.0 Mpa | ||
| Flexural modulus | ISO 178 | 2200 Mpa | |
| 50.0mmSpan | ASTM D790 | 2300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| 屈服 | ISO 527-2/50 | 4.5 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 56.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.13 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 25.0 cm3/10min |
| 260°C/5.0kg | ISO 1133 | 20.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XCY620H |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 126 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| vicat | ISO 306/B120 | 130 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| 100°C10 | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 128 °C |
| 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 106 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 108 °C | |
| vicat | ASTM D15259 | 129 °C |