Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC/ABS C2950-701 SABIC INNOVATIVE CHONGQING

CYCOLOY™

Electrical field,Electronic field,Household appliances,Household appliances,Automotive sector

Flame retardant,High mobility,High impact resistance,High temperature resistan,heat-resisting

Plastic Datasheets

combustion performance	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
Limiting Oxygen Index (LOI)	ASTM D 2863	32 %
UL fire rating 5VB	UL 94	2.49 mm
UL fire rating V	UL 94	1.5 mm

hardness	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
Hardness (Rockwell R)		ASTM D785	123 R

Electrical Property	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
Arc resistance		ASTM D495	PLC_6
Compared to the Leakage Traceability Index (CTI)		UL 746A	PLC_0
Dielectric constant		ASTM D 150	3
Dielectric strength	in oil, 3.2	ASTM D149	19.5 kV/mm
Dissipation factor		ASTM D 150	49 E-4
High current arc ignition (HAI)		UL 746A	PLC_0
High voltage arc tracing rate		UL 746A	PLC 2
Hot wire ignition (HWI)		UL 746A	PLC_1
Surface resistivity		ASTM D257	10000000000000000 Ohm
Volume resistivity		ASTM D257	100000000000000000 ohm-cm

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
Bending modulus	2.6 mm/	ASTM D790	2650 Mpa
bending strength	2.6 mm/，Yield	ASTM D790	102 Mpa
Elongation at Break	Type I, 50	ASTM D638	40
tensile strength	Type I, 50，Yield	ASTM D638	62 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
melt mass-flow rate		ASTM D1238	10 g/10min
Shrinkage rate	xflow, 3.2	Internal	0.4-0.6
Shrinkage rate		flow, 3.2	Internal	0.4-0.8
Water absorption rate	24 hours	ASTM D570	0.1
Water absorption rate		flow, 3.2	ASTM D570	0.4

impact performance	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
Impact strength of cantilever beam gap	30℃	ASTM D256	160 J/m
Impact strength of cantilever beam gap		23℃	ASTM D256	534 J/m
Instrumented dart impact energy 23 ℃ (73 ℉) total energy		ASTM D3763	61 J
Instrumented dart impact energy -30 ℃ (-22 ℉) peak		ASTM D3763	54 J

thermal properties	Test Condition	Test Method	SABIC INNOVATIVE CHONGQING/C2950-701
Linear coefficient of thermal expansion	-30°C to 3，Across Flow	ASTM E831	72 E-6/°C
Linear coefficient of thermal expansion		-30°C to 3，Flow	ASTM E831	72 E-6/°C
RTI Elec		UL 746B	85 °C
RTI Imp		UL 746B	85 °C
thermal conductivity		ASTM C 177	0.2 W/m-°C
Vicat softening temperature	Rate B/50	ASTM D1525	85 °C