ABS TP90 TORAY JAPAN
Toyolac®
Industrial machinery、Fitness equipment
transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 100 J/m |
| 23°C,12.7mm | ASTM D256 | 140 J/m |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 10 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 10 % |
| bending strength | 23°C | ISO 178 | 55.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 40.0 Mpa |
| bending strength | ASTM D790 | 56.0 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 1490 Mpa |
| ASTM D790 | 1690 Mpa | ||
| tensile strength | ASTM D638 | 32.0 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 8E+09 ohms | |
| static decay | 23°C | 内部方法 | 0.3 sec |
| ElectrostaticVoltage | 23°C | 内部方法 | 300 V |
| optical performance | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| Haze ratio | 3000µm | ISO 14782 | 17 % |
| transmissivity | 总计,3000µm | ISO 13468 | 73.0 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.11 g/cm³ |
| ASTM D792 | 1.11 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 31 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/TP90 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 78.0 °C |