Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TSU-Ether InnoTuf® HP-2160A Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2160A |
|---|---|---|---|
| Thermosetting components | 硬化法 | 按重量计算的混合比:43按容量计算的混合比:46 | |
| 树脂 | 按重量计算的混合比:100按容量计算的混合比:100 | ||
| 脱模时间(66°C) | 180to300 min |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2160A |
|---|---|---|---|
| Viscosity | 固化时间(25°C) | 1.7E+02 hr | |
| 25°C4 | 3.6 Pa·s | ||
| GelTime | 10to20 min | ||
| 25°C2 | 0.34 Pa·s | ||
| 25°C3 | 1.7 Pa·s |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2160A |
|---|---|---|---|
| tear strength | ASTM D624 | 22.8 kN/m | |
| elongation | 断裂 | ASTM D638 | 150 % |
| tensile strength | ASTM D638 | 6.21 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 55to65 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2160A |
|---|---|---|---|
| density | Hardener | 0.990 g/cm³ | |
| 基体树脂 | 1.08 g/cm³ | ||
| Cured | 1.02 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.20to0.50 % |