PEI 1010FC-7101 SABIC INNOVATIVE US
ULTEM™ 
food
High temperature resistan、enhance、Flame retardant、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
Impact strength of cantilever beam gap-30°CISO 180/1A5.0 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Impact strength of cantilever beam gap23°CISO 180/1A5.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
ball-indentation hardnessH 358/30ISO 2039-1140 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
Tensile modulusISO 527-2/13200 Mpa
tensile strength 屈服ISO 527-2/50105 Mpa
bending strengthISO 178160 Mpa
Flexural modulusISO 1783300 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 转轮内部方法10.0 mg
Tensile strain断裂ISO 527-2/5060 %
屈服ISO 527-2/506.0 %
tensile strength 断裂ISO 527-2/5085.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
dielectric strength1.60 mm, 在油中IEC 60243-128 KV/mm
relative permittivity50 HzIEC 602502.90
Dissipation Factor1 MHzIEC 602506.0E-3
Compared to the Leakage Tracking Index (CTI)解决方案 BIEC 60112 V
--IEC 60112 V
Volume resistivityIEC 600931.0E+15 ohms·cm
Dissipation Factor60 HzIEC 602505.0E-4
relative permittivity1 MHzIEC 602502.90
Dissipation Factor50 HzIEC 602505.0E-4
2.45 GHzIEC 602502.5E-3
Surface ResistivityIEC 60093> 1.0E+15 ohms
relative permittivity60 HzIEC 602502.90
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
UL flame retardant rating3.0 mmUL 945VA
0.75 mmUL 94V-0
Burning wire flammability index3.2 mmIEC 60695-2-12960 °C
Limiting Oxygen IndexISO 4589-247 %
physical property Test ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
Water absorption rate平衡, 23°C, 50% RHISO 620.70 %
Melt volume flow rate340°C/5.0 kgISO 113313.0 cm3/10min
Shrinkage rateFlow内部方法0.50 - 0.70 %
Water absorption rate饱和, 23°CISO 621.3 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
vicat--ISO 306/B120212 °C
thermal conductivityISO 83020.21 W/m/K
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDTISO 75-2/Be195 °C
vicat--ISO 306/A50215 °C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDTISO 75-2/Ae190 °C
vicat--ISO 306/B50211 °C
Linear coefficient of thermal expansion流动 : 23 到 150°CISO 11359-25.0E-5 cm/cm/°C
RTI ImpUL 746170 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
RTIUL 746170 °C
Linear coefficient of thermal expansion横向 : 23 到 150°CISO 11359-25.0E-5 cm/cm/°C
RTI ElecUL 746170 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/1010FC-7101
drying time4.0 to 6.0 hr
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel360 to 410 °C
Temperature at the rear of the barrel350 to 400 °C
Processing (melt) temperature370 to 410 °C
Hopper temperature80 to 120 °C
drying temperature150 °C
Temperature at the front of the material cylinder370 to 420 °C
Temperature140 to 180 °C
Spray nozzle temperature360 to 410 °C