PS TOTAL Polystyrene Compound 818E 法国TOTAL石化
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 93 |
| Mechanical properties | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 40 % |
| tensile strength | 屈服 | ISO 527-2 | 20.0 MPa |
| Flexural modulus | ISO 178 | 2000 MPa |
| Electrical performance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| dielectric strength | 160 kV/mm | ||
| Surface Resistivity | IEC 60093 | >1.0E+13 ohms |
| flammability | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| Shrinkage rate | 0.40to0.70 % | ||
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 9.0 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | <0.10 % |
| density | ISO 1183 | 1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Compound 818E |
|---|---|---|---|
| vicat | ISO 306/A50 | 90.0 °C |