PLA 4032D(粉) NATUREWORKS USA
Ingeo™
chip、Laminate
Thermal stability、High mobility、standard、Updatable resources、Oil resistant、Biodegradable、Food contact compliance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | NATUREWORKS USA/4032D(粉) |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 16 J/m |
| film | Test Condition | Test Method | NATUREWORKS USA/4032D(粉) |
|---|---|---|---|
| Water Vapor Transmission Rate | ASTM F1249 | 380 g·mm/m²/atm/24 hr | |
| tensile strength | MD，屈服，25 µmMD，屈服，25 µm | ASTM D882 | 103 Mpa |
| OTr | ASTM D1434 | 675 cm³/m²/24 hr | |
| Secant modulus | MD，25 µmMD，25 µm | ASTM D882 | 3450 Mpa |
| Tensile strain | TD，断裂，25 µmTD，断裂，25 µm | ASTM D882 | 100 % |
| film thickness | 测试经测试 | 25 µm | |
| Spencer ImpactSpencer Impact | 2.5 J | ||
| Elmendorf tear strength | TD，25 µmTD，25 µm | ASTM D1922 | 14 g |
| tensile strength | TD，屈服，25 µmTD，屈服，25 µm | ASTM D882 | 145 Mpa |
| Secant modulus | TD，25 µmTD，25 µm | ASTM D882 | 3790 Mpa |
| Tensile strain | MD，断裂，25 µmMD，断裂，25 µm | ASTM D882 | 180 % |
| Carbon dioxide transmittance | 内部方法 | 2850 cm³/m²/24 hr | |
| Elmendorf tear strength | MD，25 µmMD，25 µm | ASTM D1922 | 17 g |
| optical performance | Test Condition | Test Method | NATUREWORKS USA/4032D(粉) |
|---|---|---|---|
| gloss | 20°，25.4 µm20°，25.4 µm | ASTM D2457 | 90 |
| Haze ratio | 25.4 µm25.4 µm | ASTM D1003 | 2.1 % |
| physical property | Test Condition | Test Method | NATUREWORKS USA/4032D(粉) |
|---|---|---|---|
| Melt density | 230℃230℃ | 1.08 g/cm³ | |
| melt mass-flow rate | 210℃，2.16kg210℃/2.16 kg | ASTM D1238 | 7 g/10min |
| Thermal performance | Test Condition | Test Method | NATUREWORKS USA/4032D(粉) |
|---|---|---|---|
| Crystallization peak temperature | DSCDSC12 | ASTM D3418 | 155 to 170 °C |