PA66 PLS95G35DH1 BK549 DUPONT USA
Zytel®
Fitness equipment,Automotive Applications
Glass fiber reinforced,high strength,Filler: Glass fiber reinf,35% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | DUPONT USA/PLS95G35DH1 BK549 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
-30°C | ISO 179/1eU | 70 kJ/m² |
Mechanical properties | Test Condition | Test Method | DUPONT USA/PLS95G35DH1 BK549 |
---|---|---|---|
Tensile modulus | ISO 527-2 | 11000 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
tensile strength | 断裂 | ISO 527-2 | 200 Mpa |
flammability | Test Condition | Test Method | DUPONT USA/PLS95G35DH1 BK549 |
---|---|---|---|
FMVSS flammability | FMVSS302 | B | |
Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
burning rate | 1.00mm | ISO 3795 | <100 mm/min |
physical property | Test Condition | Test Method | DUPONT USA/PLS95G35DH1 BK549 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.70 % |
MD | ISO 294-4 | 0.20 % | |
Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.0 % |
MediumDensity | 1.26 g/cm³ | ||
Ejection Temperature | 210 °C | ||
viscosity number | 96%H2SO4 | ISO 307 | 130 cm³/g |
SpecificHeatCapacity of Melt | 2300 J/kg/°C | ||
ThermalConductivityofMelt | 0.22 W/m/K | ||
Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.8 % |
Thermal performance | Test Condition | Test Method | DUPONT USA/PLS95G35DH1 BK549 |
---|---|---|---|
melting temperature | ISO 11357-3 | 265 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 261 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 242 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
TD | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
Glass Transition Temperature | ISO 11357-2 | 85.0 °C |