Properties
Certificates
LCP E5006L-BK SUMITOMO JAPAN
SUMIKASUPER®
Optical data storage、Spool
heat-resisting、enhance、Glass fiber reinforced、CLTE、Filler: Long glass fiber
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 6.40mm | ASTM D256 | 380 J/m |
| hardness | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 90 |
| Supplementary Information | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| Solder resistance | 内部方法 | 350 °C |
| Mechanical properties | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| Poisson's ratio | 7.58 0.48 | ||
| elongation | 断裂 | ASTM D638 | 4.5 % |
| tensile strength | 屈服 | ASTM D638 | 151 Mpa |
| bending strength | 屈服,23°C | ASTM D790 | 152 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 14200 Mpa |
| Electrical performance | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| dielectric constant | 1.00GHz | ASTM D150 | 3.40 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.022 |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| Dissipation Factor | 1.00GHz | ASTM D150 | 4E-03 |
| flammability | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| UL flame retardant rating | 0.30mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.020 % |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 % |
| Shrinkage rate | TD | 内部方法 | 0.86 % |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/E5006L-BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 355 °C |
| Linear coefficient of thermal expansion | MD:150°C | 内部方法 | 1.7E-05 cm/cm/°C |
| TD:150°C | 内部方法 | 7.3E-05 cm/cm/°C | |
| thermal conductivity | JISR2618 | 0.54 W/m/K |