Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS VH-0815T Samsung Cheil South Korea
STAREX®
Automotive components、Household appliances
High impact resistance、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/VH-0815T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 22 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 19 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/VH-0815T |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 104 |
| R级 | ASTM D785 | 100 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/VH-0815T |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2000 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 45.0 Mpa |
| elongation | 断裂 | ASTM D638 | 17 % |
| Tensile modulus | ISO 527-2/50 | 2200 Mpa | |
| bending strength | ISO 178 | 71.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ASTM D790 | 59.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 27.0 Mpa |
| 屈服 | ASTM D638 | 39.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 8.0 % |
| Flexural modulus | ASTM D790 | 2200 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 33.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/VH-0815T |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/VH-0815T |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.8 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.34-0.41 % |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 4.2 g/10min |
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.36-0.44 % |
| TD：3.20mm | ASTM D955 | 0.36-0.44 % | |
| MD:3.20mm | ISO 2577 | 0.34-0.41 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/VH-0815T |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 71.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 77.0 °C | |
| vicat | -- | ISO 306/B120 | 88.0 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 81.0 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 79.0 °C | |
| vicat | -- | ISO 306/B50 | 86.0 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 84.0 °C |