ABS/PMMA BF-0670 BK22101 Samsung Cheil South Korea
STAREX®
Automotive components、Casters、Electronic and electrical、Electrical appliances
High temperature resistan、Aging resistance、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/BF-0670 BK22101 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.4 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/BF-0670 BK22101 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 115 |
| R级 | ASTM D785 | 114 | |
| Hardness | --7 | JISK5401 | F |
| --6 | JISK5401 | F |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/BF-0670 BK22101 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2080 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 52.0 Mpa |
| elongation | 断裂 | ASTM D638 | 18 % |
| Tensile modulus | ISO 527-2/50 | 2500 Mpa | |
| bending strength | ISO 178 | 70.0 Mpa | |
| Flexural modulus | ISO 178 | 2360 Mpa | |
| bending strength | ASTM D790 | 66.7 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 36.3 Mpa |
| 屈服 | ASTM D638 | 49.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 22 % |
| Flexural modulus | ASTM D790 | 2350 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 36.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/BF-0670 BK22101 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 2.0mm | UL 94 | HB | |
| 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/BF-0670 BK22101 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.30 % |
| TD:3.20mm | ISO 2577 | 0.40 % | |
| TD：3.20mm | ASTM D955 | 0.30 % | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 25 g/10min |
| 220°C/10.0kg | ISO 1133 | 24 g/10min | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.40 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/BF-0670 BK22101 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 72.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 80.0 °C | |
| vicat | -- | ISO 306/B120 | 92.0 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 83.0 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 86.0 °C | |
| vicat | -- | ISO 306/B50 | 92.090.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 90.0 °C |
| 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 92.0 °C |