Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Polyarylate U-polymer U-8000 UNITIKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 110 J/m |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 125 |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 110 % |
| tensile strength | ASTM D638 | 71.0 MPa | |
| compressive strength | ASTM D695 | 86.0 MPa | |
| Flexural modulus | ASTM D790 | 2700 MPa | |
| bending strength | ASTM D790 | 103 MPa |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | ASTM D257 | 2E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 44 kV/mm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.015 |
| arc resistance | ASTM D495 | 120 sec |
| optical performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 87.0 % |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.80 % |
| Water absorption rate | 24hr,3.18mm | ASTM D570 | 0.15 % |
| density | ASTM D792 | 1.26 g/cm³ |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer U-8000 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6.2E-05 cm/cm/°C |