PP K9017 FCFC TAIWAN
TIRIPRO®
container,Bumper,parts
UV resistance,High mobility,High impact resistance
UL
TDS
Processing
MSDS
UL
RoHS
SVHC
PSC
FDA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/K9017 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | NoBreak |
| -20°C,3.18mm | ASTM D256 | 81 J/m |
| hardness | Test Condition | Test Method | FCFC TAIWAN/K9017 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 76 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/K9017 |
|---|---|---|---|
| Flexural modulus | 23°C | ASTM D790A | 883 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 20.6 Mpa |
| elongation | 断裂,23°C | ASTM D638 | >200 % |
| flammability | Test Condition | Test Method | FCFC TAIWAN/K9017 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/K9017 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 17 g/10min |
| density | ASTM D792 | 0.900 g/cm³ | |
| Shrinkage rate | MD：23°C | 内部方法 | 1.4-1.8 % |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/K9017 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,6.35mm，HDT | ASTM D648 | 98.0 °C |