PPA HTNFE350064 BK544 DUPONT USA
Zytel®
--
Filler: Carbon fiber rein,15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTNFE350064 BK544 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 48 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HTNFE350064 BK544 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10400 Mpa | |
| bending strength | ISO 178 | 240 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.4 % |
| Flexural modulus | ISO 178 | 8700 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 168 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTNFE350064 BK544 |
|---|---|---|---|
| Volume resistivity | ASTM D4496 | 1E+05 ohms·cm |
| flammability | Test Condition | Test Method | DUPONT USA/HTNFE350064 BK544 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/HTNFE350064 BK544 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.50 % |
| MD | ISO 294-4 | 0.20 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/HTNFE350064 BK544 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 300 °C | |
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| TD：-- | ISO 11359-2 | 8.3E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 1.7E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.4E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 8.5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 258 °C |