Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BESTPOLUX PC02 TRIESA SPAIN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TRIESA SPAIN/BESTPOLUX PC02 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 19 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 无断裂 |
| 23°C | ISO 179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | TRIESA SPAIN/BESTPOLUX PC02 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric strength | IEC 60243-1 | 18 kV/mm | |
| Surface Resistivity | IEC 60093 | <1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | TRIESA SPAIN/BESTPOLUX PC02 |
|---|---|---|---|
| tensile strength | ISO 527-2 | 64.0 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | >80 % |
| Tensile modulus | ISO 527-2 | 2200 MPa |
| flammability | Test Condition | Test Method | TRIESA SPAIN/BESTPOLUX PC02 |
|---|---|---|---|
| burning rate | FMVSS302 | <100 mm/min | |
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TRIESA SPAIN/BESTPOLUX PC02 |
|---|---|---|---|
| humidity | 颗粒 | ISO 1110 | 0.20 % |
| melt mass-flow rate | ISO 1133 | 15 g/10min | |
| Shrinkage rate | ISO 294-4 | 0.60 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.24 % |
| density | ISO 1183 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | TRIESA SPAIN/BESTPOLUX PC02 |
|---|---|---|---|
| vicat | ISO 306 | 145 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 140 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 135 °C |