Mechanical properties	Test Condition	Test Method	LANXESS GERMANY/NP2H-AT
Flexural modulus	2mm/min 80×10×4	ISO 178	2300 Mpa
Impact strength of cantilever beam gap	-20℃	ISO 180/1A	- kJ/m²
elongation at break	50mm/min	ISO 527	20 %
bending strength	2mm/min 80×10×4	ISO 178	68 Mpa
Tensile modulus	1mm/min	ISO 527	2400 Mpa
Rockwell hardness	t=6.4mm	ISO 2039-2	111 R标尺
Impact strength of cantilever beam gap	23℃	ISO 180/1A	17 kJ/m²
melt mass-flow rate	220℃；10kg	ISO 1133	37 g/10min
Tensile stress	50mm/min，屈服	ISO 527	43 Mpa
tensile strength	50mm/min	ISO 527	33 Mpa

physical property	Test Condition	Test Method	LANXESS GERMANY/NP2H-AT
Heat distortion temperature	1.80Mpa，HDT	ISO 75	- °C
density		ISO 1183	1.05 g/cm³
Heat distortion temperature	0.45Mpa，HDT	ISO 75	- °C

Thermal performance	Test Condition	Test Method	LANXESS GERMANY/NP2H-AT
vicat	50N:120K/h	ISO 306	94 °C
UL flame retardant rating	1.6mm	UL 94	HB 类别