Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2010MPH 9001 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Fiber grade
enhance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 4500 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 2700 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 135 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.9 % |
| Flexural modulus | ISO 178 | 4000 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2900 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2 | 78.0 Mpa |
| elongation at break | ASTM D638/ISO 527 | 10 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3 - 0.5 % | |
| density | ASTM D792/ISO 1183 | 1.26 |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| process temperature | 280-300 °C | ||
| Dry conditions | 热风干燥 120℃---約4-8小时 | ||
| screw speed | 50-100 rpm | ||
| Temperature | 80-120 °C |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.40-0.60 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.30-0.50 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.14 % |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2010MPH 9001 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 145 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 140 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.7E-05 cm/cm/°C | |
| ASTM D696/ISO 11359 | 5.8.E-05 mm/mm.℃ |
Contact Us
Get App
Top