Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CF-3300HF Samsung Cheil South Korea
INFINO®
Phone、Electronic and Electrical
High rigidity、Antichemical、Filler: Glass fiber reinf、Filler: Glass fiber reinf
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/CF-3300HF |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 18 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 150 J/m |
| 23°C | ISO 180/1A | 17 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 180 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/CF-3300HF |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 115 |
| R级 | ASTM D785 | 115 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/CF-3300HF |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 6400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 125 Mpa |
| elongation | 断裂 | ASTM D638 | 3.8 % |
| Tensile modulus | ISO 527-2/50 | 6900 Mpa | |
| bending strength | ISO 178 | 180 Mpa | |
| Flexural modulus | ISO 178 | 7300 Mpa | |
| bending strength | ASTM D790 | 170 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 120 Mpa |
| 屈服 | ASTM D638 | 120 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.8 % |
| Flexural modulus | ASTM D790 | 6500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 125 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/CF-3300HF |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-1 |
| 0.8mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/CF-3300HF |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.10-0.30 % |
| TD:3.20mm | ISO 2577 | 0.10-0.30 % | |
| TD：3.20mm | ASTM D955 | 0.10-0.30 % | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 22 g/10min |
| density | ASTM D792 | 1.40 g/cm³ | |
| ISO 1183 | 1.40 g/cm³ | ||
| melt mass-flow rate | 250°C/10.0kg | ISO 1133 | 22 g/10min |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.10-0.30 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/CF-3300HF |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 138 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 140 °C | |
| vicat | -- | ISO 306/B120 | 148 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 143 °C |
| vicat | -- | ISO 306/B50 | 147 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 143 °C |