Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT+PET POCAN® ECO T 3220 000000 德国朗盛
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3220 000000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 35 kJ/m² |
| 23°C | ISO 180/1U | 35 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | <10 kJ/m² |
| -30°C | ISO 179/1eA | <10 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 35 kJ/m² |
| Supplementary Information | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3220 000000 |
|---|---|---|---|
| ISO Shortcut | ISO 7792 | PBT+PET.GHMR.09-070.GF20 |
| Electrical performance | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3220 000000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3220 000000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.2 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 MPa |
| bending strength | 3.5%Strain | ISO 178/A | 195 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 7500 MPa |
| Flexural modulus | 23°C | ISO 178/A | 7500 MPa |
| bending strength | 23°C | ISO 178 | 195 MPa |
| FlexuralStrainatFlexuralStrength5(23°C) | 3.5 % |
| physical property | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3220 000000 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % |
| density | 23°C | ISO 1183 | 1.47 g/cm³ |
| Shrinkage rate | MD:270°C,2.00mm2 | ISO 294-4 | 0.40 % |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 15.0 cm³/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 1.0 % |
| MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| Thermal performance | Test Condition | Test Method | 德国朗盛/POCAN® ECO T 3220 000000 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225to250 °C | |
| MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C | |
| vicat | ISO 306/B120 | 210 °C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C |
| TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |