PA66 66 FVT 30 NAT A Dilaplast S.p.A.
--
--
Filler, glass fiber reinforced material, 30%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Dilaplast S.p.A./66 FVT 30 NAT A |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 6.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Dilaplast S.p.A./66 FVT 30 NAT A |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| tensile strength | 屈服 | ISO 527-2 | 120 MPa |
| Flexural modulus | ISO 178 | 6.50 MPa |
| Electrical performance | Test Condition | Test Method | Dilaplast S.p.A./66 FVT 30 NAT A |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric strength | ASTM D149 | 20 kV/mm |
| flammability | Test Condition | Test Method | Dilaplast S.p.A./66 FVT 30 NAT A |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
| physical property | Test Condition | Test Method | Dilaplast S.p.A./66 FVT 30 NAT A |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| density | ISO 1183 | 1.37 g/cm³ |
| Thermal performance | Test Condition | Test Method | Dilaplast S.p.A./66 FVT 30 NAT A |
|---|---|---|---|
| vicat | ISO 306/B50 | 220 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 220 °C |